On the Fatigue Damage of 7 : 3 Brass Specimens under Combined Stress


ファイル 記述 サイズフォーマット
JSME11_48_958.pdf1.02 MBAdobe PDF本文ファイル

タイトル: On the Fatigue Damage of 7 : 3 Brass Specimens under Combined Stress
著者: Matake, Tomokazu
発行日: 1968年12月
出版者: 社団法人日本機械学会
引用: Bulletin of JSME. 1968, 11(48), p.958-962
抄録: Following the previous paper (under reversed bending and torsion), fatigue damage of 7 : 3 brass specimens under combined stress is researched by 'annealing-electropolishing method'. Standard damage life, N_0,is decided under two stress levels respectively. According to the results, fatigue damage concentrates on the surface of the specimen. N_0 becomes shorter rapidly, as σ_n becomes greater, which is normal stress on the plane of maximum shearing stress. If the ratio of number of stress repetitions to N_0 is constant, then the depth of fatigue damage layer is constant also under various stress states. Knowing N_0 under reversed torsion, the depth of fatigue damage is decided using an emprical formula, under various stress states.
URI: http://hdl.handle.net/10069/16739
ISSN: 00213764
関連リンク : http://ci.nii.ac.jp/naid/110002361283/
権利: 社団法人日本機械学会 / 本文データは学協会の許諾に基づきCiNiiから複製したものである
資料タイプ: Journal Article
原稿種類: publisher
出現コレクション:060 学術雑誌論文

引用URI : http://hdl.handle.net/10069/16739

このリポジトリに保管されている文献はすべて著作権により保護されています。
印刷やダウンロード等データの複製は、調査研究・教育または学習を目的とする場合に限定されます。

 

Valid XHTML 1.0! Copyright © 2006-2015 長崎大学附属図書館 - お問い合わせ Powerd by DSpace