Remanence enhancement based on L1[sub 0] ordering in Fe-Pt permanent magnets


ファイル 記述 サイズフォーマット
JouApplPhy9_3435.pdf423.15 kBAdobe PDF本文ファイル

タイトル: Remanence enhancement based on L1[sub 0] ordering in Fe-Pt permanent magnets
著者: Tanaka, Y. / Hisatsune, K.
発行日: 2003年 3月
出版者: American Institute of Physics
引用: Journal of Applied Physics, 93(6), pp. 3435-3439; 2003
抄録: This study investigated the relationship between the hard magnetic properties and microstructure of bulk FePt magnets, which can potentially be used in dental prostheses. A high level of remanence was obtained in a Fe-39.5 mol %Pt alloy aged at 873 K, in which minute FePt ordered domains of about 10 nm in size were uniformly created. The change in the maximum energy product of this alloy was in good agreement with the level of remanence: they both decreased with increasing aging time, and the size of the ordered domains gradually grew. The remanence ratio of as-quenched Fe-40 mol %Pt magnet has been estimated at 0.69, despite the morphological isotropy of the magnet. Remanence enhancement occurred in an FePt single phase without the presence of the magnetically soft disordered phase, since the spring back phenomenon was not observed in the recoil curve measurements, and the entire area was covered with minute FePt ordered domains. The hard magnetic properties were enhanced at the optimum ordered domain size of about 10 nm. This study found that the ordered domains behaved as a single magnetic domain particle and improved remanence through intergranular exchange interaction. ©2003 American Institute of Physics.
URI: http://hdl.handle.net/10069/21940
ISSN: 00218979
DOI: 10.1063/1.1555675
関連リンク : http://link.aip.org/link/?JAPIAU/93/3435/1
権利: Copyright (2003) American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in J. Appl. Phys. 93, 3435 (2003) and may be found at http://link.aip.org/link/?JAPIAU/93/3435/1
資料タイプ: Journal Article
原稿種類: publisher
出現コレクション:060 学術雑誌論文

引用URI : http://hdl.handle.net/10069/21940

このリポジトリに保管されている文献はすべて著作権により保護されています。
印刷やダウンロード等データの複製は、調査研究・教育または学習を目的とする場合に限定されます。

 

Valid XHTML 1.0! Copyright © 2006-2015 長崎大学附属図書館 - お問い合わせ Powerd by DSpace