500℃付近における鉄と溶融亜鉛との反応について


ファイル 記述 サイズフォーマット
kogaku00_07_11.pdf3.53 MBAdobe PDF本文ファイル

タイトル: 500℃付近における鉄と溶融亜鉛との反応について
その他のタイトル: The Reactions between Solid Iron and Liquid Zinc at Temperatures of so-called "Linear Range"
著者: 古賀, 秀人 / 内山, 休男 / 安芸, 隆房 / 深堀, 博史
著者(別表記) : Koga, Hideto / Uchiyama, Yasuo / Aki, Takafusa / Fukahori, Hirofumi
発行日: 1976年 7月
出版者: 長崎大学工学部 / Faculty of Engineering, Nagasaki University
引用: 長崎大学工学部研究報告, (7), pp.79-86; 1976
抄録: The reactions between solid iron and liquid zinc at temperatures of so-called "linear range" were studied by dipping the pure iron specimen into the pure molten zinc. At 490℃, the alloy layers consist of a I layer next to the iron, followed by a δ1 layer, a ζ layer and a zinc layer. The ζ layer disappeared at long immersion time, and a (δ1 +η) mixture formed. The growth of each alloy layer seems to be unsystematically, but the total amount of iron reacted with zinc (Fe (total)) and the amount of iron diffused into the alloy layers (Fe (in alloy layer)) varied with immersion time according to the parabolic rate law. At 500℃ and 510℃, the alloy layers consist of a I layer next to the iron, followed by a δ1 layer, a (δ1+η) layer and a zinc layer. The ζ phase didn't form even at short immersion time. The total thickness of the alloy layers and the thickness of the (δ1+η)layer varied with immersion time according to the rate law faster than the parabolic rate law. Therefore, it seems that the (δ1+η) layer grows not only by diffusion mechanism, but also by zinc penetration. The Fe (total) and Fe (in alloy layer) varied with immersion time according to the linear rate law roughly, but the latter became constant as the (δ1+η) layer dropped off into the molten zinc. The amount of iron dissolved into the molten zinc (Fe (in molten zinc)) is proportional to (immersion time)O.8 for every immersion temperatures. It is remarkable that the variation of Fe (in molten zinc) for 490℃ is similar to that for "linear range".
URI: http://hdl.handle.net/10069/23860
ISSN: 02860902
資料タイプ: Departmental Bulletin Paper
原稿種類: publisher
出現コレクション:第7号

引用URI : http://hdl.handle.net/10069/23860

このリポジトリに保管されている文献はすべて著作権により保護されています。
印刷やダウンロード等データの複製は、調査研究・教育または学習を目的とする場合に限定されます。

 

Valid XHTML 1.0! Copyright © 2006-2015 長崎大学附属図書館 - お問い合わせ Powerd by DSpace