Preparation of β-sialon from Silica-gel


ファイル 記述 サイズフォーマット
KJ00000136535.pdf379.71 kBAdobe PDF本文ファイル

タイトル: Preparation of β-sialon from Silica-gel
著者: Uchiyama, Yasuo / Tasaki, Hideyuki / Kobayashi, Kazuo / Sano, Hideaki
発行日: 2001年 1月
引用: 長崎大学工学部研究報告 Vol.31(56) p.137-141, 2001
抄録: To prepare β-sialon (Si_2Al_4O_4N_4) through alumino-thermite reaction, white silica-gel with amorphous structure was reacted with aluminum at 1400℃ to 1800℃ for 0.5 to 4.0h under nitrogen gas flow. The molar ratio of SiO_2 to Al was 12 : 16 and cobalt of 8 mass% against white silica-gel was added as a reaction promoter. Sialon (Si_<6-z>Al_zO_zN_<8-z>) with the z-value ranging from 2.5 to 4.0 was formed at 1400℃ and 1600℃. Aluminum compounds such as α-Al_2O_3,AIN and others were formed along with sialon at these temperatures. The reason why many aluminum compounds were formed is considered to be caused by volatilization of silicon as SiO gas. On the other hand, Al_2O_3・AIN spinel and AIN were formed at 1800℃, except sialon.
URI: http://hdl.handle.net/10069/5148
ISSN: 02860902
資料タイプ: Departmental Bulletin Paper
出現コレクション:第31巻 第56号

引用URI : http://hdl.handle.net/10069/5148

このリポジトリに保管されている文献はすべて著作権により保護されています。
印刷やダウンロード等データの複製は、調査研究・教育または学習を目的とする場合に限定されます。

 

Valid XHTML 1.0! Copyright © 2006-2015 長崎大学附属図書館 - お問い合わせ Powerd by DSpace