Formation Mechanism of Aluminum Nitride Powder via Organic Precursor Prepared from Anhydrous Aluminum Chloride and Ethylenediamine


ファイル 記述 サイズフォーマット
KJ00000136625.pdf479.46 kBAdobe PDF本文ファイル

タイトル: Formation Mechanism of Aluminum Nitride Powder via Organic Precursor Prepared from Anhydrous Aluminum Chloride and Ethylenediamine
著者: Kano, Masataka / Hyodo, Takeo / Shimizu, Yasuhiro / Egashira, Makoto
発行日: 2002年 7月
引用: 長崎大学工学部研究報告 Vol.32(59) p.185-190, 2002
抄録: Synthesis of AlN powder via an organic precursor prepared from anhydrous aluminum chloride and ethylenediamine has been investigated to establish a simple and low-cost process. A brownish white solid product precipitated rapidly by simply mixing anhydrous aluminum chloride into ethylenediamine at room temperature in flowing dry N_2. Any crystallized compounds were not formed from the resulting organic precursor after calcination at 800℃ for 5 h in flowing dry N_2,but formation of amorphous AlN was suggested from the FT-IR spectroscopic analysis. Crystallized AlN powder could be synthesized from the precursor after calcination at 1200℃ for 5 h in flowing dry N_2. The crystallite size of AlN powder was less than 25 nm, but the particle size was in the range of 60-100 μm due to agglomeration of fine particles under the present synthesis conditions.
URI: http://hdl.handle.net/10069/5230
ISSN: 02860902
資料タイプ: Departmental Bulletin Paper
出現コレクション:第32巻 第59号

引用URI : http://hdl.handle.net/10069/5230